uhp600 than chì điện cực phân tích và giải pháp cho cuối khối rơi trong EAF luyện kim

1. Many steel plants encounter the problem of end block falling to some extent during the smelting of steel billets. During EAF smelting, the current of UHP600 electrode can reach around 90,000A, and the current density can reach about 25A/cm². In the process of smelting, the mặt cắt ngang area of UHP600 will dần giảm. Under constant current conditions, with a reduction in in electrode cross-sectional area and an boost in current density, the loading capacity of the electrode tăng. Combined with the strength exerted by the bottom part of electric arc furnace on electrodes, both external force and internal force acting on on. Do đó, nứt có thể xảy ra as well as end block falling or detachment. If this situation occurs and we continue to maintain a constant current while aiming to improve production capacity and output, it is invitable that blocks at the bottom part will fall off.

 

2. Các yếu tố ảnh hưởng kết thúc khối rơi hoặc tách ra bao gồm% 3a quá khổ máy biến áp công suất% 3b ba pha mất cân bằng% 3b quá mức cao thứ cấp điện áp% 3b quá mức cao thứ cấp dòng điện% 3b quá mức dầu tiêu thụ.

 

3. Giải pháp: Dần dần tăng hiện tại trong luyện quá trình để giảm tiêu thụ tỷ lệ. As nóng chảy tiến trình, dần mỏng ra điện cực đầu đầu cho đến khi chúng siêu phàm đi doe to xói mòn từ nóng chảy xỉ (mà xâm nhập vào nóng chảy hồ bơi). Tất nhiên% 2c điện cực tiêu thụ là chặt chẽ liên quan đến thiết kế đặc điểm và hoạt động điều kiện cụ thể đến mỗi điện hồ quang lò đơn vị liên quan in này khoảng thời gian - đột ngột tăng in điện dòng điện nên tránh như như nhiều như có thể kể từ khi làm vì vậy hiệu quả giảm điện cực tiêu thụ tỷ lệ.